Simultaneous production of furfural and levulinic acid from pine sawdust via acid-catalysed mechanical depolymerization and microwave irradiation
2019
In this work pine sawdust was converted into levulinic acid (LA) and furfural. Sawdust was first pre-treated with sulfuric acid-catalysed mechanical depolymerization. The conversion reactions were then performed with microwave heating at 180 °C. To enhance the furfural yield and the efficient separation of furfural and LA, a biphasic water-toluene reaction system was used. The effect of an additional catalyst, AlCl3, on the yield of LA and furfural was also studied. According to the results the pre-treatment method enhanced the yields of LA. In addition, due to the microwave heating the reaction times were short. Additional AlCl3 catalyst enhanced the LA yield, however excellent furfural yi…
Rapid one-step solvent-free acid-catalyzed mechanical depolymerization of pine sawdust to high-yield water-soluble sugars
2017
Abstract One-step absolute solvent-free acid-catalyzed mechanical depolymerization of pine sawdust (PSD) and commercially available α-cellulose to water-soluble sugars was carried out using ball milling. For comparison purposes, the commonly reported “solvent-free” mechanocatalytic depolymerization of lignocellulose method, which normally involves three steps (acid impregnation in solvent, vacuum drying, and mechanical depolymerization of lignocellulose), was performed. The 3,5-dinitrosalicylic acid (DNS) method was used to measure the total reducing sugar (TRS) of the obtained sugar solution, and major monosaccharides in the solution were analyzed by capillary electrophoresis (CE). More th…
Simultaneous production of furfural and levulinic acid from pine sawdust via acid-catalysed mechanical depolymerization and microwave irradiation
2019
Abstract In this work pine sawdust was converted into levulinic acid (LA) and furfural. Sawdust was first pre-treated with sulfuric acid-catalysed mechanical depolymerization. The conversion reactions were then performed with microwave heating at 180 °C. To enhance the furfural yield and the efficient separation of furfural and LA, a biphasic water-toluene reaction system was used. The effect of an additional catalyst, AlCl3, on the yield of LA and furfural was also studied. According to the results the pre-treatment method enhanced the yields of LA. In addition, due to the microwave heating the reaction times were short. Additional AlCl3 catalyst enhanced the LA yield, however excellent fu…